"Jinan Huifeng aluminium Co., LTD", established from the year 2006, is a newly aluminum processing production enterprise, restructured from state-run enterprise , located in China's" Rose Town "—PingYing county of Jinan city territory.
Product Overviews
Aluminum profiles/extrusions
Jinan Huifeng Aluminum Co.,Ltd professionally manufacture and export many kinds of aluminum industrial profiles.
We supply aluminum seamless tube and other industrial profiles, we manufacture them according to customer's CAD drawing. We can provide full range services of aluminum profiles, including: extrusion, machining and anodizing, have a wide range of commercial alloys, 2A12, 2014, 2014A, 2017A, 2024, 3003, 5A02, 5083, 6005A, 6060, 6061, 6063, 6082, 6463, 7020, 7075 etc ,subject to temper requirements and product specification.
Main Alloy | 2014,2017,5052,6061,6063,7075,7A04 etc. |
Tempter | H112,T4,T6 etc. |
Finish | Mill Finish,Anodization etc. |
Specification | According to CAD drawing or customer’s requirements |
MOQ | 1 tons |
Payment | TT or LC at sight |
Delivery time | Approx 45 days according to different products |
Usages | Different purposes mainly for industrial usages |
Main products of aluminum profiles
performance
CHEMICAL COMPOSITION OF EN AW-6061 [Al Mg1SiCu] | ||||||||||
SI | FE | CU | MN | MG | CR | NI | ZN | TI | ZR | AL |
0.4-0.80 | 0.70 | 0.15-0.40 | 0.15 | 0.8-1.20 | 0.04-0.35 | --- | 0.25 | 0.15 | --- | Remainder |
MECHANCIAL PROPERTY OF 6061 ALUMINUM PROFILES | |||||||
Temper | Measurement (mm) Wall Thickness | Rm (Mpa) Yield Strength | Rp0.2 (Mpa) Tensile Strength | Elongation | |||
Min | Max | Min | Max | A % Min | A50mm % Min | ||
T4 | ≤25 | 180 | 110 | ---- | 15 | 13 | |
T6 | ≤5 | 260 | ---- | 240 | ---- | 9 | 7 |
T6 | 5<e≤25 | 260 | ---- | 240 | --- | 10 | 8 |
T-Temper Main Designations
Alloys that are precipitation hardened gain their strength by solution heat treating (SHT) and ageing. Of the nine different tempers, T3, T6 and T7 are perhaps the most important.
Cooled from elevated temperature shaping process > Naturally aged to a substantially stable condition | |
Cooled from elevated temperature shaping process > Cold worked > Naturally aged | |
Solution heat treated > Cold worked > Naturally aged | |
Solution heat treated > Naturally aged | |
Cooled from high temperature shaping > Artificially aged | |
Solution heat treated > Artificially aged | |
Solution heat treated > Overaged (i.e. beyond maximum strength) | |
Solution heat treated > Cold worked > Artificially aged | |
Solution heat treated > Artificially aged > Cold worked |
equipment
The main equipment including 3600 tons to 800 tons extruding machine, tension straightening machine, 11 rollers straighter, tube drawing mill, rod drawing machine, 400 KW vertical quench furnace and six tube rolling mill production lines; Ancillary equipment including nitriding furnace, homogeneous furnace, and ageing oven, eight set of intermediate frequency induction furnace and oxidation ponds.